Product

Armor-Coat™ Epoxy Hard Coat is a two component, easy to mix, 1A to 1B by volume medium viscosity epoxy and is specially formulated for use as a bonding agent. Armor-Coat provides superior adhesion to new or existing surfaces. It comes in clean, easy to use plastic pails.

Armor-Coat will bond to most concrete, wood, fiberglass and metal surfaces. Armor-Coat is resistant to moisture and most chemicals and solvents. Armor-Coat is also excellent for bonding and laminating or used as a filler/patching compound when mixed with our Polygem Thickening Agent.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: 4,000 cps
• Working Time: 70 min.* (100 gms)
• Cure Time: 48 Hours
• Shore Hardness: 86D
• Mixed Color: Gray (color may vary)

The LCR Crack Repair kit contains enough material to repair an average 1/16" wide, eight foot crack. LCR is ideal for homeowners, contractors, remodelers, maintenance personnel and D.I.Y. users. Dispenses with standard 10 oz caulking gun not included.

The LCR Crack Repair Kit contains:

• Two ten-ounce cartridges of liquid injection repair epoxy
• Pint of A & B crack sealer pastes
• Seven injection ports

LCR™ Epoxy Injection Resin is a 100% solids, two-component, moisture insensitive epoxy designed to permanently restore structure and design strength to cracked concrete structures. Unique wetting properties allow maximum penetration of LCR into cracks above .005”. LCR liquid concrete repair injection epoxy can be used on wet or dry surfaces, as well as underwater.

TECHNICAL SPECIFICATIONS

• Working Time: 55 min.(73°F - 23°C)
• Cure Time: 90 min. (73°F - 23°C)
• Working Time: 30 min. (73°F - 23°C)
• Thin Film Set Time: 2-3 hrs. (73°F - 23°C)
• Full Cure Time: 24 hrs.
• Compressive Strength: 7,908 psi (ASTM D-695)
• Compressive Modulus: 135 ksi (ASTM D-695)
• Tensile Strength: 5,868 psi (ASTM D-698)
• Flexural Modulus: 270 ksi (ASTM D-790)
• Flexural Strength: 948 psi (ASTM D-790)
• Elongation at Break: 2.73% (ASTM D-638)
• Shrinkage:.0.001 in./in.
• Heat Deflection Temp: (at 66 psi) 120 °F (49 °C)
• Shore D Hardness: 80D (ASTM D2240)
• Low Viscosity Cartridge (LV): 580 cps
• High Viscosity Cartridge (HV): 1,910 cps

LCR Liquid Concrete Repair Injection Ports are affixed to the surface of the crack to provide for the injection of the LCR - Liquid Injection Epoxy Resin to fill and seal cracked concrete foundation walls. Bag of 7.

LCR™ EPOXY REPAIR PASTE is a high strength two-component, moisture insensitive epoxy with many uses. The paste bonds easily to concrete, wood, metal, fiberglass, plastic, glass and more. It can be purchased separately and also as part of our LCR™ Basement Foundation Crack Repair Kit.

LCR Epoxy Repair Paste can be used to adhere tiles, make household repairs and as a bonding adhesive for hobby and craft projects. It is also an excellent material for anchoring, patching, grouting and crack repair.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 60 min. (100g)
• Thin Film Working Time: 1 Hour
• Full Cure Time: 16 Hours
• Shore Hardness: 81D
• Color: Grey
• Compressive Strength: 6,798 psi (ASTM D695)
• Compressive Modulus: 157 psi (ASTM D695)
• Tensile Strength: 2323 psi (ASTM D638)
• Elongation at Break: 0.35% (ASTM D638)
• Shrinkage: 0.0001 in./in.
• Heat Deflection Temp: 115 °F (46 °C) (ASTM C882)

1002FS™ Epoxy Crack Paste is a fast-setting, epoxy paste designed for sealing cracked concrete prior to injection with epoxy or urethane resin systems. With a simple 1A to 1B mix ratio by volume, it is easy to use and will be ready for injection in as little as 25 minutes. 1002FS is ideal for setting injection ports and can also be used for patching concrete prior to top-coating. It bonds strongly to damp surfaces and will cure hard even on cold, wet walls. The thick, non-sag paste formula makes it excellent for vertical and overhead applications.

TECHNICAL SPECIFICATIONS

• Pot Life: 4 min (100 g - ASTM D-2471)
• Mix Ratio: 1A : 1 by volume
• Tack Free Time: 10 min (100g)
• Full Cure Time: 25 min.
• Shore D Hardness: 83D (ASTM D2240)
• Mixed Viscosity: Heavy Paste
• Mixed Color: Warm Light Grey

PolyFM™ Injection Grouts are hydrophobic polyurethane injection grouts designed to permanently seal water leaks and fill voids in concrete and masonry structures. Upon contact with water, these resins rapidly expand to form a tough, flexible, and resilient closed-cell foam, creating a permanent watertight barrier.

PolyFM™-LV is a low viscosity, two-component resin available in convenient dual cartridges for repairing wider cracks and voids.

TECHNICAL SPECIFICATIONS

• Pot Life: 40min (100 g - ASTM D-2471)
• Mix Ratio: 1A to 1B by volume
• Mixed Viscosity: 400 cps
• Mixed Color: Amber
• Foam Expansion: Up to 10x Original Volume
• Water Absorption:: < 1% (ASTM D-2127)
• Density (Free Rise): 8 lbs/ft3 (ASTM D-1622)
• Density (Restricted): 8 lbs/ft3 (ASTM D-1622)
• Tensile (Free Rise): 320 psi (ASTM D-638)
• Elongation(Free Rise): 100% (ASTM D-638)
• Shrinkage:< 1% (ASTM D-2126)

PolyFM-1C™ Injection Grout is a high-performance blend of hydrophilic and hydrophobic polyurethane resins, engineered for reliable crack repair and void grouting. When exposed to water, it expands up to 10 times its original volume to create a permanent, flexible, and watertight seal. Easy to use and clean, PolyFM-1C eliminates the need for costly equipment or messy setups. It comes packaged in convenient 10 fl. oz. caulk-style cartridges that fit any standard caulk gun, making application fast and simple.

TECHNICAL SPECIFICATIONS

• Pot Life (once injected): 2 min. (Stays liquid in cartridge)
• Mix Ratio: Single Component
• Cure Time: 2 Hours Minimum
• Viscosity: 600 cps
• Color: Clear Amber
• Tensile Strength (Restricted): 2.02 lbs/ft³ (ASTM D-1622)
• Tensile Strength (Free Rise): 2.02 lbs/ft³ (ASTM D-1622)
• Elongation: 400% (ASTM D-638)
• Tear Strength (Restricted): 400psi (ASTM D-624)
• Tear Strength (Free Rise): 55psi (ASTM D-624)

519HT High Temp Ceramic Tile Adhesive™ is our industry standard epoxy tile adhesive for use in environments up to 400°F (204°C). 519HT is a thixotropic gel that can adhere tiles applied to vertical and overhead surfaces. 519HT is formulated to provide for a tenacious bond to most ceramic, metal, concrete, fiberglass or wood surfaces. 519HT is moisture resistant and will even cure underwater.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Gel (ASTM D2393)
• Pot Life: 30 min. (100g)
• Shore Hardness: 80D
• Color: Dark Grey
•   Part A: Charcoal | Part B: Tan VOC Content: 0%
• Thin Film Working Time: 45 mins.
• Cure Time @ 1/8 in. (3.17 mm.): 16 hrs.
• Cure Time @ 1/4 in. (6.35 mm.): 5 hrs.
• Compressive Strength: 14,000 psi (ASTM D-638)
• Tensile Strength: 6,000 psi (ASTM D-638)
• Impact (IZOD) Strength: 21 ft. lbs. (ASTM D-638)
• Operating Temperature: 350-400°F (177-204°C)

1001 Epoxy Injection Resin™is a 100% solids, two-component, moisture insensitive epoxy designed to penetrate hairline cracks in concrete structures. Unique wetting properties allow maximum penetration of 1001 EHV into cracks as small as .005 in.

TECHNICAL SPECIFICATIONS

• Pot Life: 40min (100 g - ASTM D-2471)
• Mix Ratio: 2A to 1B by volume
• Thin Film Set Time: 5-7 Hours
• Full Cure Time: 36 Hours
• Shore D Hardness: (ASTM D2240) 65-70D
• Mixed Viscosity: Non-Sag
• Mixed Color: Amber

Polygem injection ports are made from durable, chemical-resistant plastic, often translucent or clear, designed specifically for low-pressure epoxy or polurethane injection into concrete cracks, with integrated caps to manage the flow of repair materials. Package of 50.

Specifically crafted for corner cracks, ensuring precise placement and superior epoxy distribution in hard-to-reach areas., Compatible with Polygem Epoxy Systems. Optimized for use with Polygem’s high-strength Epoxy Injection System, ensuring professional-grade results in concrete repair. Made from durable, chemical-resistant, non-reactive plastic that ensures long-lasting performance.

A compact, disposable mixing nozzle designed to blend two-part polyurethane components (Part A resin and Part B hardener) as they are dispensed. With a 1/4" diameter internal flow path, it provides thorough mixing in a small, controlled stream, making it ideal for precision casting, bonding, sealing, and potting applications. The static mixing elements inside ensure consistent ratio blending, reduced air entrapment, and uniform material performance without the need for manual stirring.

A compact, disposable mixing nozzle designed to blend two-part polyurethane components as they are dispensed. With a 1/2" diameter internal flow path, it provides thorough mixing in a small, controlled stream, making it ideal for precision casting, bonding, sealing, and potting applications. The static mixing elements inside ensure consistent ratio blending, reduced air entrapment, and uniform material performance without the need for manual stirring.

Plastic retaining nut for attaching Epoxy and Foam Static Mixing Tubes. Nut fits 1/4 to 1/2 inch OD epoxy and polyurethane static mixing nozzles.

The M300LV Dispensing Gun is a high-performance manual applicator designed for dispensing low-viscosity, two-part polyurethane, epoxy, and silicone materials from dual-cartridge systems. Built for smooth operation and precise control, it ensures accurate mixing and consistent material flow when used with compatible static mixing nozzles. Its durable construction makes it ideal for casting, bonding, sealing, and potting applications where reliable dispensing and repeatable results are required.

The M300X Dispensing Gun is a heavy-duty manual applicator engineered for dispensing medium- to high-viscosity, two-part polyurethane, epoxy, and silicone materials from dual-cartridge systems. Designed for strength, durability, and consistent performance, it delivers precise control and reliable material flow when paired with compatible static mixing nozzles. Ideal for demanding casting, bonding, sealing, and potting applications, the M300X ensures accurate dispensing and uniform results in professional and industrial environments

1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion. 1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 35 mins. (100g)
• Cure Time: 16-24 Hours
• Shore Hardness: 80-85D
• Color: Grey
• Compressive Strength: 10,600 psi (ASTM D695)
• Compressive Modulus: 308,000 psi (ASTM D695)
• Tensile Strength: 8,300 psi (ASTM D638)
• Elongation at Break:3% min. (ASTM D638)
• Bond Strength:2,000 psi (ASTM C882)

519HT-WB™ Wearing Compound is an epoxy paste blended with abrasion resistant large (16-20 Mesh) white ceramic beads that was specially formulated to provide protection in areas subjected to wear and abrasion in elevated temperature conditions. High temperatures will contribute to premature failure of many polymers, but the 519HT-WB will provide a durable barrier of protection up to 450 degrees Fahrenheit intermittent exposure. 519HT-WB is an easy-to-mix 1:1 by volume ratio, is waterproof and resistant to most chemicals and solvents. 519HT-WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 40 min. (100g)
• Cure Time: 4-5 Hours
• Shore Hardness: 78D
• Color Mixed: Grey
• Compressive Strength: 7,583 psi (ASTM D695)
• Compressive Modulus: 183 ksi (ASTM D695)
• Tensile Strength: 1,422 psi (ASTM D638)
• Elongation at Break: 0.17% (ASTM D638)
• Flexural Modulus: 524 ksi (ASTM D790)
• Flexural Strength: 3,254 psi (ASTM D790)
• Taber Wear Index: 125.44 (ASTM D4060-10 | MIL-8625F)

PG Clear™ Silicone is a strong, one-part sealant and adhesive that cures at room temperature for lasting performance. Once set, it forms waterproof, airtight bonds on metal, glass, tile, wood, fiberglass, marble, painted surfaces, aluminum, and many more. Its UV-resistant, all-weather formula works indoors or out and holds up in tough conditions from -62 to 350°F (-52 to 177°C), with intermittent exposure up to 400°F (204°C). Safe and VOC-compliant, it meets today’s Green Building Standards.

Ideal for repairs, sealing, and bonding a wide range of common materials in construction, home improvement, and industrial settings.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Clear
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter

GelFoam™ Injection Grout is an innovative and simple to use hydrophilic polyurethane resin system designed to provide the ultimate solution for crack repair and void grouting applications. In contact with water, GelFoam will expand up to 20 times its original volume creating a permanent, flexible and water tight seal. GelFoam eliminates the need for costly equipment and messy cleanups. GelFoam™ is a super low viscosity, single component resin that is ideal for sealing fine cracks.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A to 1 Part Water By Volume
• Working Time: 60 sec.(73°F - 23°C)
• Cure Time: 90 min. (73°F - 23°C)
• Viscosity: 230 cps
• Tensile Strength: 375 psi (ASTM D-1623)
• Elongation: 410% (ASTM D-1623)
• Shear Strength: 175 psi (ASTM D-273)
• Color: Milky White

Granite Flex™ Epoxy Adhesive is a flexible adhesive, specially formulated to provide up to 40% elongation when cured. This flexibility allows for thermal expansion, vibration absorption, and substrate movement without bond failure, while maintaining durable and reliable adhesion performance.

Granite Flex™ is ideally suited for bonding ceramic tile, stone, and masonry in demanding industrial or agricultural environments, as well as for countertop assembly and structural joint repair. Its solvent-free, water-cleanable formulation makes it practical to apply and safe to use in enclosed spaces.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Pot Life: 4 Hours (100g) (ASTM D2471)
• Cure Time: 16 Hours
• Shore Hardness: 45D (ASTM D2240)
• Color: Light Tan
• Die C Tear Strength: 83 pli
• Specific Volume (Mixed): 17.55 cu in/lb (ASTM D792)
• Tensile Strength: 823 psi (ASTM D638)
• Elongation at Break: 40% (ASTM D638)

PolyFM™ Injection Grouts are hydrophobic polyurethane injection grouts designed to permanently seal water leaks and fill voids in concrete and masonry structures. Upon contact with water, these resins rapidly expand to form a tough, flexible, and resilient closed-cell foam, creating a permanent watertight barrier.

PolyFM™-SLV is a super low viscosity, single component resin that is ideal for sealing fine cracks.

TECHNICAL SPECIFICATIONS

• Pot Life: 6min (100g - ASTM D-2471)
• Mix Ratio: Single Component
• Cure Time: 45 min.
• Viscosity: 200 cps
• Color: Amber
• Solids Content: 100%
• Density (Free Rise): 2.02 lbs/ft³ (ASTM D-1622)
• Elongation: 60% (ASTM D-1623)
• Tensile Strength: 29 psi (ASTM D-1623)
• Shrinkage:0% (ASTM D-2126)

PG RedHT™ Silicone is a premium one-part high temp adhesive sealent that withstands extreme heat from -62 to 500°F (-52 to 260°C), with intermittent exposure to 650°F (343°C). It bonds tightly to metal, tile, glass, ceramic, and more—creating strong, waterproof, and airtight seals. Ideal for demanding jobs indoors or out, it’s weather-resistant, VOC-compliant, and meets Green Building Standards.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Red
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter

307 Ceramic Tile Adhesive™ is our industry standard epoxy tile adhesive. For use in environments up to 400°F (204°C). 307 is a thixotropic gel that can adhere tiles applied to vertical and overhead surfaces. 307 Tile Adhesive is formulated to provide for a tenacious bond to most ceramic, metal, concrete, fiberglass or wood surfaces. 307 Tile Adhesive is moisture resistant and will even cure underwater.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste (ASTM D2393)
• Pot Life: 60 min. (100g)
• Shore Hardness: 81D
• Color: Dark Grey
• Working Time: 30min.
• Thin Film Working Time: 45 mins.
• Full Cure Time: 16 hrs.
• Compressive Strength: 6,798 psi (ASTM D-695)
• Compressive Modulus: 157 psi (ASTM D-695)
• Tensile Strength: 2323 psi (ASTM D-638)
• Elongation at Break: 0.35% (ASTM D-638)
• Shrinkage: 0.0001 in./in.
• Heat Deflection Temp: 115°F (46°C) (ASTM C882)

1618 Clear™ Epoxy Coating is a low viscosity, easy to mix, two-component epoxy sealer and top coat with a 2A to 1B by volume mix ratio. It’s low viscosity formula allows for easy to spread thin-coat applications. 1618 Clear is resistant to most chemicals and solvents. It is non-blushing and works well even in cool or humid conditions. 1618 Clear has many uses and is the goto material within many industries.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 2A:1B by volume
• Mixed Viscosity: 2000 cps
• Working Time: 28 min (100 gms)
• Thin Film Working Time: 2 Hours
• Cure Time: 48 Hours
• Shore Hardness: 60D
• Mixed Color: Clear

1001 Epoxy Injection Resin™is a 100% solids, two-component, moisture insensitive epoxy designed to penetrate hairline cracks in concrete structures. Unique wetting properties allow maximum penetration of 1001-LV into cracks as small as .005 in.

TECHNICAL SPECIFICATIONS

• Pot Life: 45min (100 g - ASTM D-2471)
• Mix Ratio: 2A to 1B by volume
• Thin Film Set Time: 2-3 Hours
• Full Cure Time: 24 Hours
• Shore D Hardness: (ASTM D2240) 80D
• Mixed Viscosity: 580 cps
• Mixed Color: Amber

307FR Lite II™ is a lightweight, two-component trowelable epoxy system that is E-84 Class A Flame-Rated and public space safe- It has an easy-to-mix, “paste-like” consistency that is commonly used for general fabrication, coating, sculpting, patching, filling, joining, and repair. It contains no VOCs and is solvent-free. 307FR Lite II cures to a hard, strong, durable material suitable for interior and exterior spaces and themed environments.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Paste
• Working Time:
•   Spreadable: 1 Hour
•   Stampable: 2 Hours
•   Sculptable: 3 Hours
• Cure Time: 16 Hrs.
• Shore Hardness: 77D
• Color: Light Brown/Tan (color may vary)

307 Lite™ Sculpting Epoxy is a lightweight, two-component trowelable epoxy system that is public space safe- It is formulated as an easy-to-mix, “paste-like” consistency that is commonly used for general fabrication, coating, sculpting, patching, filling, joining, and repair. It contains no VOCs and is solvent-free. 307 Lite cures to a hard, strong, durable material that is easy to sand or machine and is suitable for interior and exterior spaces and themed environments.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Thick Paste
• Pot Life: 90 mins (100 grams)
• Working Time:
•   Spreadable: 1 Hour
•   Stampable: 1.5 Hours
•   Sculptable: 2 Hours
• Cure Time: 16 Hrs.
• Shore Hardness: 78D
• Color: Gray (color may vary)

Polygem Thickening Agent™ is a lightweight, inert filler designed to increase the viscosity of 307 series Epoxy systems. When blended into the mixed epoxy, it enhances workability by reducing sag and improving control during vertical or overhead applications. The additive also helps reduce surface tack, making the epoxy easier to shape and apply. Ideal for sculpting, bonding, and patching tasks that require precision and stability. Store in a dry environment and use at 73°F (23°C) for the best results.

307FR Lite Flex II™ Sculpting Epoxy is a two-component, semi-rigid epoxy system that is E-84 Class A Flame-Rated and public space safe- It is available in BLACK or TAN and is formulated to be an easy-to-mix “putty-like” consistency that is commonly used to create display elements that are semi-rigid and extremely tough. 307FR Lite Flex II is also great for industrial bonding applications. It is solvent free and contains no VOCs.

307FR Lite Flex II cures to a strong and semi-flexible, material with excellent impact and abrasion resistance. Cured 307FR Lite Flex II withstands freeze/thaw cycles when used for exterior projects.

Use to make perfectly detailed tree branches, planks and other themed elements for zoos and amusement parks. Because finished elements are semi-rigid, reptiles and birds can comfortably grip them without affecting the material.

Also available in Black on a made by request basis.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Putty
• Working Time: 1 hour (100 grams)
• Cure Time: 24 Hours
• Shore Hardness: 90A
• Color: Gray (color may vary)

307 Stone™ Sculpting Epoxy is a 100% solids epoxy system specially formulated to a workable “clay-like” consistency for sculpting and modeling projects. 307 Stone will cure to an extremely strong and durable plastic with a slightly textured stone-like surface that can be easily sanded or shaped. 307 Stone is easy to mix and apply by hand or with a trowel or spatula. It can be tinted, painted or even stained.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Clay-like
• Working Time: 1 Hour (100 gms)
• Cure Time: 8 Hours
• Mixed Color: Gray (color may vary)

EZ-Karve™ Sculpting Epoxy is a 100% solids epoxy system designed with a unique clay-like consistency, making it ideal for sculpting and modeling applications. Once cured, it forms a lightweight, exceptionally strong and impact-resistant material that can be easily shaped, sanded or carved.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Clay-Like
• Pot Life: 75 mins. (100 gms)
• Cure Time: 8 Hrs.
• Color: Beige (color may vary)

1003FS™ Epoxy Crack Paste is a specially formulated low-odor epoxy paste that will provide a fast setting compound for sealing of cracked concrete prior to injection with epoxy or urethane resin systems. 1003FS has an easy to mix 1 A to 1B by volume mix ratio and will be ready for injection in as little as 25 minutes. 1003FS is ideal for setting of injection ports and can be used to patch concrete prior to top-coating. It is waterproof and will bond to wet surfaces and can even cure underwater. 1003FS is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Pot Life: 7 min.
• Tack Free Time: 10 min. (73°F/23°C @ 100 g)
• Full Cure Time: 30 min.
• Shore Hardness: 80D
• Mixed Color: Light Grey

Aqua-Gem™ Water Based Epoxy Primer is a water-based epoxy coating specially formulated for use as a surface primer for seamless flooring applications to provide superior adhesion of epoxy and urethane top-coats. Aqua-Gem is an easy to mix 1 Part A to 2 Parts B by volume mix ratio. Aqua-Gem is ideal for damp and porous concrete surfaces. Aqua-Gem is resistant to most chemicals and solvents. Aqua-Gem can be pigmented for color coating of surfaces.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:2B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 50 min. (100g)
• Thin Film Recoat Time: 4-5 Hours
• Thin Film Set Time: 6 Hours
• Full Cure Time: 18 Hours
• Shore Hardness: 75D
• Mixed Color: Clear Amber
• Elongation at Break: 0.35% (ASTM D638)
• Mixed Viscosity: 1,300 cps