1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion. 1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.
TECHNICAL SPECIFICATIONS
Mix Ratio: 1A:1B by volume
Mixed Viscosity: Heavy Paste
Working Time: 35 mins. (100g)
Cure Time: 16-24 Hours
Shore Hardness: 80-85D
Color: Grey
Compressive Strength: 10,600 psi (ASTM D695)
Compressive Modulus: 308,000 psi (ASTM D695)
Tensile Strength: 8,300 psi (ASTM D638)
Elongation at Break:3% min. (ASTM D638)
Bond Strength:2,000 psi (ASTM C882)
Description
1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion.
1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.
ADVANTAGES
Extremely durable ceramic matrix
Chemical Resistant
No VOCs or Solvents
Low Odor Formula
Bonds to most dry surfaces
RECOMMENDED USES
For the patching and repair of worn metal or concrete surfaces that are exposed to abrasive environments. 1004FS is ideal for use on:
Cyclones
Wear Plates
Hopper and Chutes
Pipe Elbows
Vibrating Screens & Beams
Pump Casings
Brick Corners & Transition Areas
Dust Collection Systems
Pneumatic Conveyors
Chipper and Grain Bins
Heat Exchangers and Tube Sheets
Augers, Fan and Impeller Blades
Videos
Technical Specifications
Typical Properties. All values measured after 7 days at 73°F (23°C).