1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion. 1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 35 mins. (100g)
• Cure Time: 16-24 Hours
• Shore Hardness: 80-85D
• Color: Grey
• Compressive Strength: 10,600 psi (ASTM D695)
• Compressive Modulus: 308,000 psi (ASTM D695)
• Tensile Strength: 8,300 psi (ASTM D638)
• Elongation at Break:3% min. (ASTM D638)
• Bond Strength:2,000 psi (ASTM C882)

519HT-WB™ Wearing Compound is an epoxy paste blended with abrasion resistant large (16-20 Mesh) white ceramic beads that was specially formulated to provide protection in areas subjected to wear and abrasion in elevated temperature conditions. High temperatures will contribute to premature failure of many polymers, but the 519HT-WB will provide a durable barrier of protection up to 450 degrees Fahrenheit intermittent exposure. 519HT-WB is an easy-to-mix 1:1 by volume ratio, is waterproof and resistant to most chemicals and solvents. 519HT-WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 40 min. (100g)
• Cure Time: 4-5 Hours
• Shore Hardness: 78D
• Color Mixed: Grey
• Compressive Strength: 7,583 psi (ASTM D695)
• Compressive Modulus: 183 ksi (ASTM D695)
• Tensile Strength: 1,422 psi (ASTM D638)
• Elongation at Break: 0.17% (ASTM D638)
• Flexural Modulus: 524 ksi (ASTM D790)
• Flexural Strength: 3,254 psi (ASTM D790)
• Taber Wear Index: 125.44 (ASTM D4060-10 | MIL-8625F)

PG Clear™ Silicone is a strong, one-part sealant and adhesive that cures at room temperature for lasting performance. Once set, it forms waterproof, airtight bonds on metal, glass, tile, wood, fiberglass, marble, painted surfaces, aluminum, and many more. Its UV-resistant, all-weather formula works indoors or out and holds up in tough conditions from -62 to 350°F (-52 to 177°C), with intermittent exposure up to 400°F (204°C). Safe and VOC-compliant, it meets today’s Green Building Standards.

Ideal for repairs, sealing, and bonding a wide range of common materials in construction, home improvement, and industrial settings.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Clear
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter

PG RedHT™ Silicone is a premium one-part high temp adhesive sealent that withstands extreme heat from -62 to 500°F (-52 to 260°C), with intermittent exposure to 650°F (343°C). It bonds tightly to metal, tile, glass, ceramic, and more—creating strong, waterproof, and airtight seals. Ideal for demanding jobs indoors or out, it’s weather-resistant, VOC-compliant, and meets Green Building Standards.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Red
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter

PolyFM™ Injection Grouts are hydrophobic polyurethane injection grouts designed to permanently seal water leaks and fill voids in concrete and masonry structures. Upon contact with water, these resins rapidly expand to form a tough, flexible, and resilient closed-cell foam, creating a permanent watertight barrier.

PolyFM™-LV is a low viscosity, two-component resin available in convenient dual cartridges for repairing wider cracks and voids.

TECHNICAL SPECIFICATIONS

• Pot Life: 40min (100 g - ASTM D-2471)
• Mix Ratio: 1A to 1B by volume
• Mixed Viscosity: 400 cps
• Mixed Color: Amber
• Foam Expansion: Up to 10x Original Volume
• Water Absorption:: < 1% (ASTM D-2127)
• Density (Free Rise): 8 lbs/ft3 (ASTM D-1622)
• Density (Restricted): 8 lbs/ft3 (ASTM D-1622)
• Tensile (Free Rise): 320 psi (ASTM D-638)
• Elongation(Free Rise): 100% (ASTM D-638)
• Shrinkage:< 1% (ASTM D-2126)

PolyFM-1C™ Injection Grout is a high-performance blend of hydrophilic and hydrophobic polyurethane resins, engineered for reliable crack repair and void grouting. When exposed to water, it expands up to 10 times its original volume to create a permanent, flexible, and watertight seal. Easy to use and clean, PolyFM-1C eliminates the need for costly equipment or messy setups. It comes packaged in convenient 10 fl. oz. caulk-style cartridges that fit any standard caulk gun, making application fast and simple.

TECHNICAL SPECIFICATIONS

• Pot Life (once injected): 2 min. (Stays liquid in cartridge)
• Mix Ratio: Single Component
• Cure Time: 2 Hours Minimum
• Viscosity: 600 cps
• Color: Clear Amber
• Tensile Strength (Restricted): 2.02 lbs/ft³ (ASTM D-1622)
• Tensile Strength (Free Rise): 2.02 lbs/ft³ (ASTM D-1622)
• Elongation: 400% (ASTM D-638)
• Tear Strength (Restricted): 400psi (ASTM D-624)
• Tear Strength (Free Rise): 55psi (ASTM D-624)

PolyFM™ Injection Grouts are hydrophobic polyurethane injection grouts designed to permanently seal water leaks and fill voids in concrete and masonry structures. Upon contact with water, these resins rapidly expand to form a tough, flexible, and resilient closed-cell foam, creating a permanent watertight barrier.

PolyFM™-SLV is a super low viscosity, single component resin that is ideal for sealing fine cracks.

TECHNICAL SPECIFICATIONS

• Pot Life: 6min (100g - ASTM D-2471)
• Mix Ratio: Single Component
• Cure Time: 45 min.
• Viscosity: 200 cps
• Color: Amber
• Solids Content: 100%
• Density (Free Rise): 2.02 lbs/ft³ (ASTM D-1622)
• Elongation: 60% (ASTM D-1623)
• Tensile Strength: 29 psi (ASTM D-1623)
• Shrinkage:0% (ASTM D-2126)