1003FS™ Epoxy Crack Paste is a specially formulated low-odor epoxy paste that will provide a fast setting compound for sealing of cracked concrete prior to injection with epoxy or urethane resin systems. 1003FS has an easy to mix 1 A to 1B by volume mix ratio and will be ready for injection in as little as 25 minutes. 1003FS is ideal for setting of injection ports and can be used to patch concrete prior to top-coating. It is waterproof and will bond to wet surfaces and can even cure underwater. 1003FS is a thick non-sag paste compound that will allow for vertical and overhead patching.
TECHNICAL SPECIFICATIONS
Mix Ratio: 1A:1B by volume
Mixed Viscosity: Heavy Paste
Pot Life: 7 min.
Tack Free Time: 10 min. (73°F/23°C @ 100 g)
Full Cure Time: 30 min.
Shore Hardness: 80D
Mixed Color: Light Grey
Description
1003FS™ Epoxy Crack Paste is a specially formulated low-odor epoxy paste that will provide a fast setting compound for sealing of cracked concrete prior to injection with epoxy or urethane resin systems. 1003FS has an easy to mix 1 A to 1B by volume mix ratio and will be ready for injection in as little as 25 minutes. 1003FS is ideal for setting of injection ports and can be used to patch concrete prior to top-coating. It is waterproof and will bond to wet surfaces and can even cure underwater. 1003FS is a thick non-sag paste compound that will allow for vertical and overhead patching.
ADVANTAGES
Easy to Mix
Fast 7 Minute Working Time
30 Minute Cure
Will Bond to Damp Surfaces
RECOMMENDED USES
1003FS Epoxy Crack Paste is used primarily for the setting of injection ports and sealing crack surfaces. It is ideal to use for:
Epoxy & Urethane Injection for repairing Concrete
Sea Wall or Underwater Concrete Repair
Aquarium & Pool Repairs
Videos
Technical Specifications
Typical Properties. All values measured after 7 days at 73°F (23°C).
Mix Ratio: 1A:1B by volume
Mixed Viscosity: Heavy Paste
Pot Life: 7 min.
Tack Free Time: 10 min. (73°F/23°C @ 100 g)
Full Cure Time: 30 min.
Shore Hardness: 80D
Mixed Color: Light Grey
Elongation at Break: 0.1% (ASTM D638)
Compressive Strength: 7,075 psi (ASTM D695)
Compressive Modulus: 144 ksi (ASTM D695)
Tensile Strength: 807 psi (ASTM D638)
Heat Deflection Temp: 135-140°F / 57-60 °C (ASTM D790)