Backing & Wear Compounds
-
1183WB™ Wearing CompoundCeramic Beaded Abrasion Resistant Wearing CompoundLearn More1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion. 1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.
TECHNICAL SPECIFICATIONS
- Mix Ratio: 1A:1B by volume
- Mixed Viscosity: Heavy Paste
- Working Time: 35 mins. (100g)
- Cure Time: 16-24 Hours
- Shore Hardness: 80-85D
- Color: Grey
- Compressive Strength: 10,600 psi (ASTM D695)
- Compressive Modulus: 308,000 psi (ASTM D695)
- Tensile Strength: 8,300 psi (ASTM D638)
- Elongation at Break:3% min. (ASTM D638)
- Bond Strength:2,000 psi (ASTM C882)
-
519HT-WB™ Wearing CompoundHigh Temperature Large White Ceramic Bead Wearing CompoundLearn More519HT-WB™ Wearing Compound is an epoxy paste blended with abrasion resistant large (16-20 Mesh) white ceramic beads that was specially formulated to provide protection in areas subjected to wear and abrasion in elevated temperature conditions. High temperatures will contribute to premature failure of many polymers, but the 519HT-WB will provide a durable barrier of protection up to 450 degrees Fahrenheit intermittent exposure. 519HT-WB is an easy-to-mix 1:1 by volume ratio, is waterproof and resistant to most chemicals and solvents. 519HT-WB is a thick non-sag paste compound that will allow for vertical and overhead patching.
TECHNICAL SPECIFICATIONS
- Mix Ratio: 1A:1B by volume
- Mixed Viscosity: Heavy Paste
- Working Time: 40 min. (100g)
- Cure Time: 4-5 Hours
- Shore Hardness: 78D
- Color Mixed: Grey
- Compressive Strength: 7,583 psi (ASTM D695)
- Compressive Modulus: 183 ksi (ASTM D695)
- Tensile Strength: 1,422 psi (ASTM D638)
- Elongation at Break: 0.17% (ASTM D638)
- Flexural Modulus: 524 ksi (ASTM D790)
- Flexural Strength: 3,254 psi (ASTM D790)
- Taber Wear Index: 125.44 (ASTM D4060-10 | MIL-8625F)