Mining & Industrial

1183WB™ Wearing Compound is a specially formulated epoxy paste blended with abrasion resistant small black ceramic beads to provide a durable barrier to protect surfaces subjected to wear and abrasion. 1183WB is an easy to mix 1A : 1B by volume ratio which is waterproof and resistant to most chemicals and solvents. 1183WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 35 mins. (100g)
• Cure Time: 16-24 Hours
• Shore Hardness: 80-85D
• Color: Grey
• Compressive Strength: 10,600 psi (ASTM D695)
• Compressive Modulus: 308,000 psi (ASTM D695)
• Tensile Strength: 8,300 psi (ASTM D638)
• Elongation at Break:3% min. (ASTM D638)
• Bond Strength:2,000 psi (ASTM C882)

519HT-WB™ Wearing Compound is an epoxy paste blended with abrasion resistant large (16-20 Mesh) white ceramic beads that was specially formulated to provide protection in areas subjected to wear and abrasion in elevated temperature conditions. High temperatures will contribute to premature failure of many polymers, but the 519HT-WB will provide a durable barrier of protection up to 450 degrees Fahrenheit intermittent exposure. 519HT-WB is an easy-to-mix 1:1 by volume ratio, is waterproof and resistant to most chemicals and solvents. 519HT-WB is a thick non-sag paste compound that will allow for vertical and overhead patching.

TECHNICAL SPECIFICATIONS

• Mix Ratio: 1A:1B by volume
• Mixed Viscosity: Heavy Paste
• Working Time: 40 min. (100g)
• Cure Time: 4-5 Hours
• Shore Hardness: 78D
• Color Mixed: Grey
• Compressive Strength: 7,583 psi (ASTM D695)
• Compressive Modulus: 183 ksi (ASTM D695)
• Tensile Strength: 1,422 psi (ASTM D638)
• Elongation at Break: 0.17% (ASTM D638)
• Flexural Modulus: 524 ksi (ASTM D790)
• Flexural Strength: 3,254 psi (ASTM D790)
• Taber Wear Index: 125.44 (ASTM D4060-10 | MIL-8625F)

PG Clear™ Silicone is a strong, one-part sealant and adhesive that cures at room temperature for lasting performance. Once set, it forms waterproof, airtight bonds on metal, glass, tile, wood, fiberglass, marble, painted surfaces, aluminum, and many more. Its UV-resistant, all-weather formula works indoors or out and holds up in tough conditions from -62 to 350°F (-52 to 177°C), with intermittent exposure up to 400°F (204°C). Safe and VOC-compliant, it meets today’s Green Building Standards.

Ideal for repairs, sealing, and bonding a wide range of common materials in construction, home improvement, and industrial settings.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Clear
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter

PG RedHT™ Silicone is a premium one-part high temp adhesive sealent that withstands extreme heat from -62 to 500°F (-52 to 260°C), with intermittent exposure to 650°F (343°C). It bonds tightly to metal, tile, glass, ceramic, and more—creating strong, waterproof, and airtight seals. Ideal for demanding jobs indoors or out, it’s weather-resistant, VOC-compliant, and meets Green Building Standards.

TECHNICAL SPECIFICATIONS

• Cure System: Acetoxy
• Movement Capability, %: ±25% (ASTM C-719)
• Modulus: Medium (ASTM D-412)
• Temperature Range: -62 to 350°F (-52 to 177°C)
• Intermittent Max Temp: 650°F (343°C)
• Working Time:
• Tack Free: 20 min. (73°F - 23°C)
• Full Cure Time: 24 hrs (73°F - 23°C)
• Specific Gravity: 1.04
• Extrusion Rate: 370 g/min (ASTM C-1183)
• Tensile Strength: 310 psi (ASTM D-412)
• Shore Hardness: 26A (ASTM C-661)
• Color: Red
• Elongation: 500% (ASTM D-412)
• Dielectric Strength: 20 kv/mm (500 v/mil
• Dielectric Constant: 2.7@60 (at 100 Hz)
• Volatile Organic Content: 30 gr./liter